Anti Iron Tip Erosion Super Low Ag Flux Cored Wire Solder
72M series contain new and more active activator for improved wettability and new resin composition for better flux coverage. They can prevent bridging even at bridging prone conditions such as low iron tip temperature for or fast sliding speed.
Inhibits erosion of Fe plating
Co added to S03X7Ca-72M forms a barrier layer at the iron tip surface, which inhibits erosion of the tip. S03X7Ca-72M significantly reduces wear of iron tips compared to regular lead-free solder.
Prevents bridging in slide soldering
72M series contain new activators for improved wettability and new resin composition for better flux coverage. They can prevent bridging even at defect prone conditions such as low iron tip temperature or fast sliding speed.
Ultimate cost reduction by flux-cored solder
The low Ag composition of 0.3% reduces product prices, while prevention of iron tip erosion reduces running costs. S03X7Ca-72M offers dual cost reduction effects.
Solder Wire S03X7Ca-72M Specs
| Product Name | Flux Cored Wire Solder S03X7Ca-72M |
| Product Category | Solder Wire |
| Melting Point(℃) | 217-227 |
| Halide content(%) | < 0.01 |
| Flux Content(%) | 3.2 |
| Flux Type | ROL0 (IPC J-STD-004) |
| Diameter(mm φ) | 0.3, 0.5, 0.6, 0.8, 1.0 ,1.2 |